AWS ERNiCrMo-17 / UNS N06200 — Welding wire specifications, parameters, and applications for nickel alloy fabrication.
Hastelloy C-2000 (AWS ERNiCrMo-17) is a nickel-chromium-molybdenum-copper welding wire for welding Hastelloy C-2000 alloy. The copper addition provides enhanced resistance to reducing acids, making it versatile for both oxidizing and reducing environments.
| Parameter | GTAW | GMAW |
|---|---|---|
| Shielding Gas | Argon (99.995%) | Ar + 2% He or Ar + 2% CO2 |
| Gas Flow Rate | 8-15 L/min | 15-25 L/min |
| Wire Diameter | 1.6-3.2 mm | 0.8-1.6 mm |
| Current Type | DCEN | DCEP |
| Welding Position | All positions | Flat / Horizontal |
C-2000 welding wire is used in a wide range of demanding applications:
Hangbo Alloy Group supplies C-2000 welding wire in the following forms:
| Standard | Description |
|---|---|
| AWS A5.14 | ERNiCrMo-17 |
| ISO 18274 | S Ni 6200 |
| EN ISO 18274 | S Ni 6200 |
| ASME SFA-5.14 | ERNiCrMo-17 |
| Element | Content (%) |
|---|---|
| Nickel (Ni) | Balance |
| Chromium (Cr) | 22.0 – 24.0 |
| Molybdenum (Mo) | 15.0 – 17.0 |
| Copper (Cu) | 1.3 – 1.9 |
| Iron (Fe) | 3.0 max |
| Carbon (C) | 0.01 max |
| Property | Typical Value |
|---|---|
| Tensile Strength | 690 MPa (100 ksi) min |
| Yield Strength (0.2%) | 310 MPa (45 ksi) min |
| Elongation | 40% min |
| Service Temperature | up to 1040°C (1900°F) |
Values above are typical for as-welded Hastelloy C-2000 (ERNiCrMo-17) deposited metal under AWS A5.14 classification requirements. Actual results vary with welding process, heat input and shielding gas.
Follow these practical guidelines to obtain sound, corrosion-resistant welds with this filler metal:
C-2000 adds roughly 1.6% copper, markedly improving resistance to reducing acids such as sulphuric and hydrofluoric acid, while high chromium retains oxidising-acid resistance. See the Hastelloy C-276 vs C-22 comparison for related context.
Yes. It is frequently applied as a corrosion-resistant overlay on carbon steel vessels and piping using GMAW, SAW or electro-slag strip cladding.
Not normally. The ultra-low carbon level allows as-welded service in most chemical process duties.
AWS ERNiCrMo-17 / UNS N06200 with about 22-24% chromium, 15-17% molybdenum and 1.3-1.9% copper, nickel balance and carbon held to 0.01% max. The copper addition is the key for reducing-acid resistance.
AWS A5.14 (ERNiCrMo-17), ISO/EN 18274 (S Ni 6200) and ASME SFA-5.14. Order against the AWS classification and UNS number to remove ambiguity.
TIG wire in 1.6, 2.0, 2.4 and 3.2 mm straight lengths, MIG wire on D200/D300 spools in 0.8-1.6 mm, and SAW coils in 2.4-4.0 mm.
Up to about 1040 °C (1900 °F), with the low carbon content preserving as-welded corrosion resistance.
Pure argon (99.995%) for GTAW; argon with 2% helium or 2% CO2 for GMAW.
Keep interpass temperature below 120 °C, use stringer beads, and back-purge root passes with argon. The 0.01% max carbon also minimizes carbide precipitation.
Hangbo Alloy Group supplies C-2000 (ERNiCrMo-17) welding wire with full material certifications. We ensure consistent wire quality with precise diameter control, clean surface finish, and uniform feeding performance.
For quotations, material certifications, or technical consultation, contact our sales team or call +86 166 2109 2936.
Request a quotation for C-2000 round bars, tubes, plates, or custom products. We stock standard sizes and accept custom orders.